This in vitro and in vivo study compared different topographies of Ti samples (dense, porosity of 30% and 40%) with or not CaP coating, prepared by powder metallurgy. Osteogenic cells from newborn rat calvaria were plated onto the samples and cell adhesion (24 hours), alkaline phosphatase activity (7 and 10 days) and mineralization nodules (14 days) were assessed. Sixteen rabbits were used for in vivo study. Each animal received three non-treated and three treated implants in the right or left tibia, respectively. Histometric evaluation of bone-implant contact (BIC) were assessed at 1, 2, 4 and 8 weeks. Metallographic analysis revealed porosities of 30% and 40%, with pore size ranging from 250 to 350 µm. Cell adhesion test and ALP revealed similar cell behavior, independently of topography and CaP coating (P > 0.05%). However, CaP coating combined with porosity of 40% influenced positively the mineralized matrix formation (P < 0.05%). CaP-coated implants showed higher BIC than non-CaP implants and BIC was different between the short (1 and 2 weeks) and long (4 and 8 weeks) healing periods (P < 0.05%). The results suggest that CaP coating combined with 40% porosity implants allowed greater osteogenesis in vitro and increased BIC in vivo.

Objective The aim of this paper was to evaluate the repair of onlay autogenous bone grafts covered or not covered by an expanded polytetrafluoroethylene (e-PTFE) membrane using immunohistochemistry in rats with induced estrogen deficiency. Material and Methods Eighty female rats were randomly divided into two groups: ovariectomized (OVX) and with a simulation of the surgical procedure (SHAM). Each of these groups was again divided into groups with either placement of an autogenous bone graft alone (BG) or an autogenous bone graft associated with an e-PTFE membrane (BGM). Animals were euthanized on days 0, 7, 21, 45, and 60. The specimens were subjected to immunohistochemistry for bone sialoprotein (BSP), osteonectin (ONC), and osteocalcin (OCC). Results All groups (OVX+BG, OVX+BMG, SHAM+BG, and SHAM+BMG) showed greater bone formation, observed between 7 and 21 days, when BSP and ONC staining were more intense. At the 45-day, the bone graft showed direct bonding to the recipient bed in all specimens. The ONC and OCC showed more expressed in granulation tissue, in the membrane groups, independently of estrogen deficiency. Conclusions The expression of bone forming markers was not negatively influenced by estrogen deficiency. However, the markers could be influenced by the presence of the e-PTFE membrane.